光熱療法における効率改善のためのシリカ-金ナノ粒子の調整可能な応答

Photothermal therapy (PTT) is an emerging minimally invasive approach for cancer treatment that relies on photothermal agents capable of efficiently converting near-infrared (NIR) light into localized heat. In this work, silica-gold nanostructures (SGNs) were synthesized and systematically evaluated to investigate how silica core size influences the photothermal response of the SGNs and optimize their performance as a photothermal agent. SGNs were synthesized with silica cores ranging from 54 to 244 nm in diameter and coated with gold nanoparticles of 4-10 nm in size, enabling controlled tuning of their localized surface plasmon resonance within the NIR region. The morphology and composition were characterized by SEM, TEM, and EDS; optical properties were analyzed by UV-Vis spectroscopy. The SGNs photothermal response low-power laser irradiation at 852 nm and 1310 nm and temperature changes were monitored using a thermographic camera. A maximum temperature increase of 7.1 °C was observed for SGNs with a silica core diameter of approximately 77 nm under the 852 nm laser irradiation. Numerical simulations of the absorption efficiency showed good agreement with experimental UV-Vis spectra and thermal measurements, revealing a size-dependent shift of the absorption toward longer wavelengths for larger nanostructures. These results demonstrate that the photothermal response of silica-gold nanostructures can be rationally tuned through the control of core size and gold growth parameters, providing a framework for the design of wavelength-matched photothermal agents for PTT applications.