高度なゲンタマイシン負荷キトサン/ヒドロキシアパタイト/メソポーラスSiO2スキャフォールド：薬物送達と細胞相互作用の包括的な調査
Nesa Abdian1, Seyed Omid Reza Sheykholeslami2, Mohamadreza Etminanfar3
1Sabanci University Nanotechnology Research and Application Center, Istanbul, 34956, Turkey; Sabanci University Faculty of Engineering and Natural Sciences, Istanbul, 34956, Turkey.
Abstract:
Implant-related infections associated with bone implants are a common problem, and traditional antibiotic treatments may cause side effects before the infection at the implant site is cleared. This study aims to develop a biocompatible and biodegradable scaffold that supports bone regeneration while providing localized and controlled antibiotic delivery. Chitosan/hydroxyapatite (CSHA) scaffolds reinforced with mesoporous SiO2 particles were fabricated via freeze-drying. All scaffolds exhibited interconnected pores, with pore sizes of approximately 340 μm in pure chitosan scaffolds, which decreased to around 90 μm in CSHA scaffolds containing mesoporous SiO2 particles. Adding mesoporous SiO2 particles to CSHA scaffolds improved structural strength, increasing the compressive strength from 3.8 ± 0.7 MPa to 22.1 ± 0.8 MPa. The water absorption ratio decreased from 3.9 ± 0.04 to 0.3 ± 0.07, and the 14-day degradation rate dropped from 32% to 20.8%. CSHA scaffolds containing mesoporous particles maintained cell viability above 98% after 7 days and released gentamicin in a controlled manner, with drug-release kinetics best described by the Weibull model. Antimicrobial tests showed strong antibacterial activity in the reinforced scaffolds against Escherichia coli. Overall, CSHA scaffolds with mesoporous SiO2 particles offer a promising option for bone tissue engineering and infection control at the implantation site.
さらに関連する動画
05:26Fabrication of Size-Controlled and Emulsion-Free Chitosan-Genipin Microgels for Tissue Engineering Applications
Published on: April 13, 2022
09:17Optimizing Extracellular Vesicle Delivery Using a Core-Sheath 3D-Bioprinted Scaffold for Chronic Wound Management
Published on: February 28, 2025
関連する概念動画
01:17Pore Transport and Ion-Pair Transport
Pore transport, also known as convective transport, is a process where small molecules like urea, water, and sugars rapidly cross cell membranes as though there were channels or pores in the membrane. Although direct microscopic evidence is limited but the concept of pores or channels is widely accepted based on physiological evidence. Despite the lack of direct microscopic...
01:24Site-Targeted Drug Delivery Systems: Polymeric Carriers