由{311}高指数平面部分封闭的多面体50面Cu2O微晶:合成和增强的催化CO氧化活性

Mei Leng1, Mingzhu Liu, Yibo Zhang

  • 1State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, 5625 Renmin Street, Changchun, Jilin 130022, P. R. China.

Journal of the American Chemical Society
|November 16, 2010
PubMed
概括

我们用一种基于溶液的方法合成了独特的50面铜(I) 氧化物 (Cu2O) 微晶. 这些新型微晶体对一氧化碳 (CO) 氧化具有增强的催化活性,为贵金属催化剂提供了有希望的替代品.

更多相关视频

Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production08:40

Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production

Published on: December 6, 2021

Synthesis and Performance Evaluations of ZnCoS/ZnCdS with Twin Crystal Structure for Multifunctional Redox Photocatalysis in Energy Applications09:22

Synthesis and Performance Evaluations of ZnCoS/ZnCdS with Twin Crystal Structure for Multifunctional Redox Photocatalysis in Energy Applications

Published on: July 25, 2025

相关概念视频

Heterogeneous Catalysis01:22

Heterogeneous Catalysis

Heterogeneous catalysis involves a catalyst in a different phase from the reactants. It is a process where the catalyst and the reactants are in distinct phases, typically solid and gas or liquid.Most heterogeneous catalysts are metals, metal oxides, or acids. The list includes transition metals like iron (Fe), cobalt (Co), nickel (Ni), palladium (Pd), platinum (Pt), chromium (Cr), manganese (Mn), tungsten (W), silver (Ag), and copper (Cu). These metals possess partially vacant d orbitals that...
Imperfections in Crystal Structure: Non-Stoichiometric Defects01:29

Imperfections in Crystal Structure: Non-Stoichiometric Defects

Non-stoichiometric defects refer to a type of defect in the crystal structure of a compound where the ratio of its constituent elements deviates from the ideal stoichiometric ratio. There are two main types of non-stoichiometric defects: metal excess defects and metal deficiency defects.Metal excess defects occur when there is a slight surplus of metal ions than what is required by the stoichiometric ratio of the compound. For example, heating a sodium chloride crystal in sodium vapor results...
Imperfections in Crystal Structure: Stoichiometric Point Defects01:26

Imperfections in Crystal Structure: Stoichiometric Point Defects

Schottky defects arise when some lattice points in a crystal, such as those in NaCl, remain unoccupied, creating lattice vacancies without disturbing the overall electrical neutrality of the crystal. This defect is common in ionic crystals where the positive and negative ions are similar in size, as seen in sodium chloride and cesium chloride. The presence of Schottky defects enables the crystal to conduct electricity to a small extent through an ionic mechanism. Electric fields cause nearby...