在S2-中Pb和Cd的固化机制 - - 富含活性化城市固体废物焚烧灰飞

Qi Xue1,2, Yongsheng Ji1,3, Zhanguo Ma1,3

  • 1State Key Laboratory for Geomechanics and Deep Underground Engineering, China University of Mining and Technology, Xuzhou 221116, China.

Materials (Basel, Switzerland)
|May 27, 2023
PubMed
概括

富含硫化物活性渣 (SEAAS) 在MSWI飞灰中有效地固化了诸如 (Pb) 和 (Cd) 等重金属. 这种新型材料显著提高了固化性能,解决了传统活性的局限性.

关键词:
在MSWI飞灰飞.用S2-丰富的活性废渣 (SEAAS)用S2−丰富的修改方法活性化水泥材料是一种活性化水泥材料.重金属固化固化过程中的重金属.

更多相关视频

Combining Solid-state and Solution-based Techniques: Synthesis and Reactivity of ChalcogenidoplumbatesII or IV10:42

Combining Solid-state and Solution-based Techniques: Synthesis and Reactivity of ChalcogenidoplumbatesII or IV

Published on: December 29, 2016

10.7K
Detection and Recovery of Palladium, Gold and Cobalt Metals from the Urban Mine Using Novel Sensors/Adsorbents Designated with Nanoscale Wagon-wheel-shaped Pores10:31

Detection and Recovery of Palladium, Gold and Cobalt Metals from the Urban Mine Using Novel Sensors/Adsorbents Designated with Nanoscale Wagon-wheel-shaped Pores

Published on: December 6, 2015

28.1K

相关概念视频

Pozzolans01:21

Pozzolans

Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
Fly ash is...
157
Sample Preparation for Analysis: Advanced Techniques01:08

Sample Preparation for Analysis: Advanced Techniques

Accurate analysis of complex samples often requires advanced preparation techniques to achieve reliable and reproducible results. Samples containing inorganic or organic materials can be challenging to dissolve or decompose effectively. Standard sample preparation methods include acid digestion, fusion, dry ashing, and wet digestion.
Acid digestion with strong acids is commonly used to dissolve inorganic materials that are insoluble (do not dissolve) in water. This method can be useful for...
400
Washing, Drying, and Ignition of Precipitates00:52

Washing, Drying, and Ignition of Precipitates

After filtration, the precipitate is washed to remove coprecipitated impurities and any remaining mother liquor. Colloidal precipitates, such as silver chloride, are washed with an electrolyte (such as dilute nitric acid) to prevent the peptization of the precipitate. In the case of slightly soluble precipitates, the wash solution contains a common ion to reduce solubility. Lead sulfate, which is slightly soluble in water, is washed with dilute sulfuric acid. Similarly, wash solutions may be...
981
Metallic Solids02:37

Metallic Solids

Metallic solids such as crystals of copper, aluminum, and iron are formed by metal atoms. The structure of metallic crystals is often described as a uniform distribution of atomic nuclei within a “sea” of delocalized electrons. The atoms within such a metallic solid are held together by a unique force known as metallic bonding that gives rise to many useful and varied bulk properties.
All metallic solids exhibit high thermal and electrical conductivity, metallic luster, and malleability....
18.5K
Alkali Aggregate Reaction in Concrete01:26

Alkali Aggregate Reaction in Concrete

The alkali-aggregate reaction in concrete involves natural siliceous minerals in aggregates reacting with alkaline hydroxides derived from cement alkalis. This reaction forms an alkali-silica gel that absorbs water, swells, and increases in volume, which is confined by the surrounding cement paste, creating internal pressures that crack and disrupt the concrete. The extent of expansion and damage can be partly attributed to the alkali-silica reaction's osmotic hydraulic pressure and the...
143