The Effect of Interfacial Chemical Bonding in TiO2-SiO2 Composites on Their Photocatalytic NOx Abatement Performance

The Effect of Interfacial Chemical Bonding in TiO2-SiO2 Composites on Their Photocatalytic NOx Abatement Performance

Published on: July 4, 2017

通过超声波辅助的酸盐和酸盐合剂对CaCO₃进行表面修饰

Peng Cheng^1,2, Lei Yang², Yuxiong Xie¹

¹School of Civil Engineering, Nanyang Institute of Technology, Nanyang 473004, China.

Materials (Basel, Switzerland)

|May 27, 2023

概括

使用西兰 (KH550) 和酸盐 (HY311) 合剂对碳酸 (CaCO3) 的表面修饰显著改善了其性能. 最佳条件提高了工业应用的分散性和稳定性.

科学领域:

材料科学材料科学材料科学
表面化学表面化学
纳米技术纳米技术

背景情况:

碳酸 (CaCO3) 是一种常见的无机粉末,由于水友性和油害性,工业用途有限.
表面修饰增强了CaCO3在有机材料中的分散和稳定性,增加了它的价值.

研究的目的:

为了改善CaCO3颗粒的表面特性.
为了评估西兰合剂 (KH550) 和泰坦酸合剂 (HY311) 修改的有效性.
使用响应表面分析优化修改条件.

主要方法:

使用KH550和HY311的合剂与超声波进行了CaCO3颗粒的修饰.
用油吸收值 (OAV),激活度 (AG) 和沉量 (SV) 来评估修改性能.
表面表征包括SEM,FTIR,XRD和热重力测量分析.

主要成果:

泰坦酸合剂 (HY311) 的修饰效果比合剂 (KH550) 的修饰效果更好.
超声波处理在修改过程中起到了辅助作用.
在最佳条件 (0.7% HY311,0.7% KH550,10分钟超声波时间) 中,OAV为16.65g DOP/100g,AG为99.27%,SV为0.65mL/g.

结论:

通过各种分析,证实了HY311和KH550在CaCO3表面上的成功涂层.
优化的合剂剂剂量和超声波时间显著改善了CaCO3修饰性能.
增强的CaCO3特性为更广泛的工业应用开辟了道路.

关键词:

在CaCO3CO3中.西兰合剂的合剂.表面的修改表面的修改泰坦酸盐的使用方法超声波的超声波处理方法

更多相关视频

Soft Lithographic Functionalization and Patterning Oxide-free Silicon and Germanium

Soft Lithographic Functionalization and Patterning Oxide-free Silicon and Germanium

Published on: December 16, 2011

Preparation of Silica Nanoparticles Through Microwave-assisted Acid-catalysis

Preparation of Silica Nanoparticles Through Microwave-assisted Acid-catalysis

Published on: December 16, 2013

相关概念视频

Sulfate Attack on Concrete

Sulfate Attack on Concrete

Sulfate attack on concrete is a deterioration process characterized by a whitish discoloration beginning at the edges and corners, accompanied by cracking and spalling. This phenomenon occurs when sulfates react with the components of hardened concrete, forming compounds like calcium sulfate and calcium sulfoaluminate which occupy more space than the substances they replace, causing the concrete to expand and disrupt.
Sulfates from sources like soil, groundwater, or industrial effluents...

Hydration of Cement

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...