和银注入的酸盐水泥:揭示物理化学性质和体外生物相容性

Meghan Singh¹, Chitra Shivalingam¹, Sheron Blessy¹

¹Prosthodontics, Saveetha Dental College and Hospitals, Saveetha Institute of Medical and Technical Sciences, Saveetha University, Chennai, IND.

|December 6, 2023

概括

这项研究成功地合成了和银注入的酸盐水泥,证明了其对牙科应用的生物相容性. 这种新材料显示出增强生物特性和更广泛的牙科临床应用的前景.

科学领域:

生物材料科学生物材料科学
牙科材料牙科材料
纳米技术纳米技术

背景情况:

酸水泥以密封性,生物活性和牙科适应性而闻名.
限制包括机械故障和过早退化.
加入和银等金属离子可以增强生物活性.

研究的目的:

评估和银浸生物活性酸盐水泥的生物医学潜力.
为了增强酸水泥的基本材料特性.
保持生物材料的特性,同时提高生物活性.

主要方法:

酸粉末的索尔凝合成.
连续添加四乙烯酸盐,酸,银酸和酸.
物理化学表征 (SEM,XRD,拉曼) 和体外血红相容性试验.

主要成果:

在X射线衍射中发现了晶体相 (Ag6Si2O7,Zn2SiO4,CaCO3).
拉曼光谱证实了Si-O-Si和Zn-O的结合.
SEM显示混合形态;EDS证实了Ca,Si,Zn,Ag,O,C元素.
在体外血液相容性测试证实了生物相容性.

结论:

成功合成了和银注入的酸盐水泥,证明了生物相容性.
预计和银的含有会增强骨质原生和抗菌性质.
需要进一步的体外和体内研究来验证临床应用.

关键词:

生物活性材料是生物活性材料.生物相容性生物相容性酸水泥的酸盐水泥是什么描述描述描述描述医疗保健医疗保健医疗保健具有再生性质的再生性质.

更多相关视频

Accessing the Cytotoxicity and Cell Response to Biomaterials

Accessing the Cytotoxicity and Cell Response to Biomaterials

Published on: July 8, 2021

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

相关概念视频

Hydration of Cement

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...

Additives and Fillers in Concrete

Additives and Fillers in Concrete

Additives and fillers are integral to enhancing the properties of concrete. Pozzolans and blast-furnace slag are additives or admixtures due to their reactions with calcium hydroxide released during cement hydration. Fillers, which are finely ground and similar in fineness to Portland cement, improve concrete attributes such as workability density, and reduce capillary bleeding or cracking. Some fillers possess hydraulic properties or participate in benign reactions within the cement paste.
The...