Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

369

在陶磨砂陶材料和 Veneered 牙科器之间评估粘合强度

Konstantinos Dimitriadis1, Dilshat U Tulyaganov2, Simeon Agathopoulos3

  • 1Division of Dental Technology, Department of Biomedical Sciences, University of West Attica, Athens, Greece.

European journal of oral sciences
|April 29, 2024
PubMed
概括

这项研究评估了两种带有陶 Veneer 的合金材料的粘合强度,证实两者都超过了临床使用的 ISO 9693 标准. 结果表明,对于牙科修复而言,结合强度令人满意.

关键词:
所有陶恢复所有陶恢复接口键的强度是接口键的强度.机械性能 机械性能 机械性能微观结构的微观结构齐尔科尼亚亚特里亚稳定化

更多相关视频

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

13.5K
Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)08:29

Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

Published on: January 7, 2019

11.3K

相关概念视频

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
152
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
122
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
127
Veneer01:19

Veneer

Veneer refers to a thin sheet of wood, typically produced to a thickness of about one-eighth of an inch or less. This material is crafted through various methods, the most common being rotary cutting. In this process, a log is mounted into a large lathe and spun against a knife edge, peeling off a continuous strip of wood as the knife penetrates deeper into the rotating log, creating a rotary-cut veneer.
Other veneering techniques include plain-slicing, quarter-slicing, and rift-slicing. These...
72