将含有10-MDP的复合水泥粘合到没有专门的陶原料的陶

Renato Quirino Ramos, Ben Mercelis, Mohammed H Ahmed

    The journal of adhesive dentistry
    |May 21, 2024
    PubMed
    概括

    复合水泥或原料中的功能性单体10-MDP对于强大的基与基结合至关重要,在老化后没有观察到显著的结合强度差异.

    关键词:
    衰老. 衰老. 这就是老龄化.债券的强度 债券的强度 债券的强度是一个功能性单体分子.喷沙 喷沙 喷沙 喷沙 喷沙 喷沙西兰 (Silane) 的意思是"静态的".带有三维化学的二氧化涂层.锡尔科尼亚是指一种的.

    更多相关视频

    Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

    Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

    Published on: July 21, 2014

    13.5K
    Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

    Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

    Published on: December 20, 2024

    363

    相关概念视频

    Bonding and Strength of Aggregate01:12

    Bonding and Strength of Aggregate

    The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
    149
    Porosity in Cement Paste01:18

    Porosity in Cement Paste

    The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
    The balance of water to cement in the mix is...
    126
    Pozzolans01:21

    Pozzolans

    Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
    Fly ash is...
    111
    Hydration of Cement01:24

    Hydration of Cement

    Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
    223