在3D打印的聚合物零件中确定残余应力

Residual stresses reside in a structure even after removing the original stress inducer. This phenomenon often arises from varied plastic deformations across different parts of a structure. Consider a rod stretched beyond its yield point. It will not regain its original length due to permanent deformation. Even after load removal, the rod does not entirely lose stress because of uneven plastic deformations, resulting in residual stresses. The computation of these stresses in structures is...

In the study of elastoplastic members subjected to bending moments, understanding the loading and unloading phases is crucial for assessing material behavior and structural integrity. During the loading phase, as the bending moment increases, the material initially responds elastically, adhering to Hooke's Law, where stress is directly proportional to strain. When the load exceeds the yield strength, plastic deformation occurs, resulting in permanent strain and deformation that remains even...

In materials that exhibit elastic and plastic behavior, known as elastoplastic materials, residual stresses can accumulate when these materials experience plastic deformation. This deformation arises from either high levels of shearing stress or significant strains. Residual stresses are internal stresses that persist within a material after removing the external force causing deformation. This phenomenon is demonstrated when observing the behavior of a shaft under torque; notably, the...