优化交联聚乙烯酒精的制备过程及其在泥泥中的热稳定性

Junhao Li1,2, Haochen Ai3, Qingchen Wang4

  • 1Engineering Research Center of Oil and Gas Field Chemistry, Universities of Shaanxi Provence, Xi'an Shiyou University, Xi'an 710065, China.

Gels (Basel, Switzerland)
|February 25, 2025
PubMed
概括

这项研究优化了甲基交联聚乙醇 (PVA) 作为高温油井水泥泥泥的流体损失添加剂,显著提高了热稳定性和性能.

关键词:
交叉连接 交叉连接 交叉连接流体损失添加剂的添加剂油井水泥泥泥油泥油泥泥油泥油泥油泥油泥油泥油泥聚乙醇的使用情况.

更多相关视频

Synthesis of Terpolymers at Mild Temperatures Using Dynamic Sulfur Bonds in PolyS-Divinylbenzene09:16

Synthesis of Terpolymers at Mild Temperatures Using Dynamic Sulfur Bonds in PolyS-Divinylbenzene

Published on: May 20, 2019

7.6K
Preparation of Biopolymer Aerogels Using Green Solvents08:13

Preparation of Biopolymer Aerogels Using Green Solvents

Published on: July 4, 2016

17.6K

相关概念视频

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
191
Plasticizers01:31

Plasticizers

Water-reducers, or plasticizers, are chemical admixtures used in concrete to improve strength and workability. These additives reduce the water-cement ratio without compromising workability, lower the cement content while maintaining the same workability, or increase workability to assist concrete placement in inaccessible areas.
Plasticizers function by using surface-active agents to create repulsive electrostatic forces between cement particles. This dispersion enhances the concrete's...
65
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
202
Types of Cement I01:21

Types of Cement I

Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
95
Superplasticizers01:30

Superplasticizers

Superplasticizers are advanced admixtures that enhance the workability of concrete by lowering the water content without compromising the strength of the material. These substances are highly effective water reducers, improving concrete flow, making it easier to work with, and enabling concrete to reach inaccessible areas or densely reinforced sections without mechanical vibration. The key components in superplasticizers are either sulfonated melamine or naphthalene formaldehyde condensates,...
77
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
109