装载着皮罗西卡姆的纯净和化布鲁希特水泥,用于长时间和持续的药物释放

Marcella Bini1,2, Giovanna Bruni1,2, Michela Sturini1,2

  • 1Chemistry Department, University of Pavia, Viale Taramelli 16, 27100 Pavia, Italy.

Materials (Basel, Switzerland)
|March 13, 2025
PubMed
概括

酸水泥 (CPCs) 在肌肉骨疾病方面表现有前途. 用或改进的机械性能和药物释放动力学,提供增强骨再生疗法的潜力.

关键词:
布鲁希特阶段 布鲁希特阶段酸水泥是一种酸水泥.解散率 解散率 解散率兴奋剂的使用 兴奋剂的使用机械测量 机械测量皮罗西卡姆 (Piroxicam) 是一种药物.

更多相关视频

Development and Characterization of Fusidic Acid-Loaded Alginate-Aloe vera Based Hydrogel FilmWound Healing04:09

Development and Characterization of Fusidic Acid-Loaded Alginate-Aloe vera Based Hydrogel FilmWound Healing

Published on: December 13, 2024

424
Ceramic Omnidirectional Bioprinting in Cell-Laden Suspensions for the Generation of Bone Analogs10:19

Ceramic Omnidirectional Bioprinting in Cell-Laden Suspensions for the Generation of Bone Analogs

Published on: August 8, 2022

1.8K

相关概念视频

Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
104
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate...
87
Pozzolans01:21

Pozzolans

Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
Fly ash is...
92
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
185
Types of Cement I01:21

Types of Cement I

Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
94
Pore Size Distribution01:23

Pore Size Distribution

In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
Adequate...
80