关于SW-ceramsite制备机制和脱效应的研究

Tianpeng Li1,2, Tingting Sun3, Caiyi Liu4

  • 1College of City and Architecture Engineering, Zaozhuang University, Zaozhuang, 277160, Shandong, China. tianpeng985@126.com.

Scientific reports
|March 23, 2025
PubMed
概括

这项研究从固体废物 (SW-ceramsite) 中开发了陶石,用于去除. 最佳条件产生了高性能,显示SW-ceramsite.

关键词:
脱效应的脱效应再生再生再生的过程烧结机制的烧结机制固体废弃物陶场地 固体废弃物陶场

更多相关视频

Monitoring Pedogenic Inorganic Carbon Accumulation Due to Weathering of Amended Silicate Minerals in Agricultural Soils.07:32

Monitoring Pedogenic Inorganic Carbon Accumulation Due to Weathering of Amended Silicate Minerals in Agricultural Soils.

Published on: June 4, 2021

5.0K
Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)08:29

Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

Published on: January 7, 2019

11.1K

相关概念视频

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
185
Sulfate Attack on Concrete01:29

Sulfate Attack on Concrete

Sulfate attack on concrete is a deterioration process characterized by a whitish discoloration beginning at the edges and corners, accompanied by cracking and spalling. This phenomenon occurs when sulfates react with the components of hardened concrete, forming compounds like calcium sulfate and calcium sulfoaluminate which occupy more space than the substances they replace, causing the concrete to expand and disrupt.
Sulfates from sources like soil, groundwater, or industrial effluents...
101
Preparation of Samples for Electron Microscopy01:20

Preparation of Samples for Electron Microscopy

To be visualized by an electron microscope, either transmission or scanning, biological samples need to be fixed (stabilized) so the electron beam does not destroy them and dried thoroughly (desiccated/dehydrated) so the vacuum does not affect them. Fixation needs to be done as quickly as possible because the sample properties will start changing as soon as it is removed from its natural environment. For example, in a tissue sample, the oxygen levels begin decreasing, causing an altered...
5.3K
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
199