Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins
03:02

Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins

Published on: January 17, 2025

924

瓦聚合方法对增材制造牙科树脂表面和粘合行为的影响

İrem B Yeşil Kurt1, Nursena Öztemel1, Almira A Diken Türksayar1

  • 1Department of Prosthodontics, Biruni University, Faculty of Dentistry.

Journal of oral science
|November 16, 2025
PubMed
概括

增材制造的中间树脂显示出临床上可接受的剪接强度 (SBS),液晶显示器 (L-PH) 和数字光处理 (D-AS) 的表现最好. D-AS还表现出优越的维克尔硬度数 (VHN),而表面粗度 (Ra) 在所有方法中都是可比的.

关键词:
维克斯硬度 维克斯硬度数字光处理是数字光处理.液晶显示器 液晶显示器 液晶显示器剪切键的强度 剪切键的强度立体光刻法-立体光刻法表面的粗度 表面的粗度

更多相关视频

Stereolithographic 3D Printing with Renewable Acrylates08:28

Stereolithographic 3D Printing with Renewable Acrylates

Published on: September 12, 2018

9.9K
3D Printing and In Situ Surface Modification via Type I Photoinitiated Reversible Addition-Fragmentation Chain Transfer Polymerization07:28

3D Printing and In Situ Surface Modification via Type I Photoinitiated Reversible Addition-Fragmentation Chain Transfer Polymerization

Published on: February 18, 2022

4.1K

相关概念视频

Anionic Chain-Growth Polymerization: Overview01:20

Anionic Chain-Growth Polymerization: Overview

The polymerization process that involves carbanion as an intermediate is called anionic polymerization. It is also a type of addition or chain-growth polymerization. Anionic polymerization gets initiated by a strong nucleophile such as an organolithium or a Grignard reagent. The most commonly used initiator for anionic polymerization is butyl lithium. Monomers involved in anionic polymerization must possess a vinyl group bonded to one or two electron-withdrawing groups. For instance,...
2.5K
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
3.1K
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
4.3K