在不同的沉积时间准备的铁薄膜的结构和磁性特性

Chunxia Zhou1, Liang Yan2, Biao Yan3

  • 1School of Materials, Shanghai Dianji University, Shanghai 201306, China.

Materials (Basel, Switzerland)
|January 10, 2026
PubMed
概括

这项研究探讨了沉积时间如何影响铁薄膜. 在120秒内发现了最佳的磁性,这表明了对先进材料的控制沉积的重要性.

关键词:
晶体结构 晶体结构存款时间 存款时间铁的薄膜薄膜是铁的薄膜.具有柔软的磁性属性.表面形态学 表面形态学

更多相关视频

Chemical Vapor Deposition of an Organic Magnet, Vanadium Tetracyanoethylene08:25

Chemical Vapor Deposition of an Organic Magnet, Vanadium Tetracyanoethylene

Published on: July 3, 2015

12.0K
Radio Frequency Magnetron Sputtering of GdBa2Cu3O7âˆ'ÃŽ ´/ La0.67Sr0.33MnO3 Quasi-bilayer Films on SrTiO3 STO Single-crystal Substrates06:49

Radio Frequency Magnetron Sputtering of GdBa2Cu3O7âˆ'ÃŽ ´/ La0.67Sr0.33MnO3 Quasi-bilayer Films on SrTiO3 STO Single-crystal Substrates

Published on: April 12, 2019

8.1K

相关概念视频

Ferromagnetism01:31

Ferromagnetism

Materials like iron, nickel, and cobalt consist of magnetic domains, within which the magnetic dipoles are arranged parallel to each other. The magnetic dipoles are rigidly aligned in the same direction within a domain by quantum mechanical coupling among the atoms. This coupling is so strong that even thermal agitation at room temperature cannot break it. The result is that each domain has a net dipole moment. However, some materials have weaker coupling, and are ferromagnetic at lower...
3.0K