-有机酸盐骨粘合剂重新用于牙科应用的内牙凝固

Tobias Renner¹, Laura Marx², Niclas Fleckenstein²

¹Department of Oral & Maxillofacial Plastic Surgery, Head and Neck Surgery, University Hospital Würzburg, Pleicherwall 2, 97070, Würzburg, Germany. renner_t2@ukw.de.

Clinical oral investigations

|February 4, 2026

概括

新的有机水泥显示出作为临时牙科修复的前景. 与现有材料相比,三酸水合物 (TMP ∙ xH2O) 和素 (OPLS) 的配方提供了优越的粘附性和密封性.

科学领域:

生物材料科学生物材料科学
牙科材料牙科材料
矿物有机化学矿物有机化学

背景情况:

可再吸收的矿物有机水泥被开发为骨粘合剂.
它们对于牙科应用的潜力,特别是牙周内科的临时修复,需要进行调查.

研究的目的:

评估新的-有机酸盐水泥作为内牙治疗中的临时修复材料.
将它们的机械强度,密封能力和结构完整性与传统的临时修复材料和参考粘合剂进行比较.

主要方法:

使用热处理的三酸水合物 (TMP ∙ xH2O 和 cattiite) 和有机酸盐 (酸 (OPLS) 和酸 (Na-IP6)) 制造了四种矿物有机水泥配方.
在牛牙上评估了机械强度 (剪接强度),密封能力 (甲蓝透) 和结构完整性.
性能与CavitTM和TTCP + OPLS参考粘合剂进行了比较.

主要成果:

与CavitTM (0.29 ± 0.16 MPa) 相比,OPLS + TMP ∙ xH2O配方表现出明显更高的切割键强度与牙 (4.35 ± 0.71 MPa).
这种配方还表现出有利的密封性能,与CavitTM相比.
设置pH和温度保持在临床上可接受的范围内,并且材料表征 (孔径测量,SEM,微CT) 支持其有利的形状.

结论:

400°C烧结TMP ∙ xH2O和OPLS的组合是临时牙科修复的有希望的候选者,特别是在非保留性腔内,由于其处理,稳定性和密封能力.
这些新型可再吸收的水泥为临时修复提供了粘合替代品.
潜在的未来应用包括纸封闭和穿孔修复.

关键词:

粘合性牙科材料是一种粘合性牙科材料.骨粘合剂是一种骨粘合剂.染料透试验染料透试验矿物有机水泥矿物有机水泥暂时恢复暂时恢复

更多相关视频

Application of Light-cured Dental Adhesive Resin for Mounting Electrodes or Microdialysis Probes in Chronic Experiments

Application of Light-cured Dental Adhesive Resin for Mounting Electrodes or Microdialysis Probes in Chronic Experiments

Published on: July 30, 2007

Dynamic Navigation in Endodontics: Guided Access Cavity Preparation by Means of a Miniaturized Navigation System

Dynamic Navigation in Endodontics: Guided Access Cavity Preparation by Means of a Miniaturized Navigation System

Published on: May 5, 2022

相关概念视频

Hydration of Cement

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...

Soundness of Cement

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create...

Adhesion

Adhesion

Adhesion occurs when one type of molecule is attracted to a different molecule. Water exhibits adhesive properties in the presence of polar surfaces, such as glass or cellulose in plants. For instance, when water is poured into a glass, the positively charged hydrogen molecules of water are more attracted to the negatively charged oxygen molecules in the silica than to the oxygen in neighboring water molecules.
Capillary action is a result of water’s adhesive tendencies. When a narrow...

Portland Cement

Portland Cement

Portland cement is the essential binding ingredient in concrete, made from finely ground materials including lime, iron, silica, and alumina. Lime is derived primarily from limestone, marble, marl, seashells, and clays, which also supply iron and alumina, while silica is sourced from sand, chalk, and bauxite. Contemporary manufacturing of Portland cement is a significant source of carbon dioxide emissions, prompting research into reducing its content in concrete through alternative...

Fineness of Cement

Fineness of Cement

The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...

Strength of Cement

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...