酸盐溶液pH对α-三酸颗粒式水泥的定性和血红相容性的影响

Abdulrahman Diabi1, Ryo Kishida1, Kunio Ishikawa1

  • 1Department of Biomaterials, Faculty of Dental Science, Kyushu University.

Dental materials journal
|February 23, 2026
PubMed
概括

使用较少的酸性溶液 (pH≥3) 用于α-三酸 (α-TCP) 颗粒式水泥,可以提高生物相容性,而不会影响环境. 这种优化增强了骨再生应用的潜力.

关键词:
骨头替代品 骨头替代品酸是一种酸.有颗粒状水泥的颗粒状水泥.孔隙结构 孔隙结构设置能力设置能力

更多相关视频

Biological Compatibility Profile on Biomaterials for Bone Regeneration10:28

Biological Compatibility Profile on Biomaterials for Bone Regeneration

Published on: November 16, 2018

13.4K
Direct and Indirect Culture Methods for Studying Biodegradable Implant Materials In Vitro14:49

Direct and Indirect Culture Methods for Studying Biodegradable Implant Materials In Vitro

Published on: April 15, 2022

5.7K

相关概念视频

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
1.0K
Setting Time of Cement01:12

Setting Time of Cement

The setting time of cement refers to the process of cement paste transitioning from a plastic state to a solid state. This process is crucial in construction as it dictates the timeframe for concrete placement, compaction, and finishing. The onset of this solidification is termed the initial set, indicating when the paste becomes unworkable. The final set is when the paste has solidified completely, and further handling or manipulation can no longer affect its shape. The cement strength is...
776
Roles of Electrolytes: Calcium and Phosphate01:27

Roles of Electrolytes: Calcium and Phosphate

Calcium and phosphate are essential electrolytes in the human body, with calcium being the most abundant mineral. Around 99% of the body's calcium is stored in the skeleton and teeth, forming a crystal lattice of mineral salts in combination with phosphates. Calcium plays crucial roles in various bodily functions such as blood clotting, neurotransmitter release, muscle tone maintenance, and nervous and muscle tissue excitability.
The calcium concentration in blood plasma is primarily...
1.4K
Phosphate Buffer01:22

Phosphate Buffer

The phosphate buffer system is a critical biological mechanism for maintaining pH stability in the body. This system operates primarily through two components: sodium dihydrogen phosphate (NaH2PO4), which acts as a weak acid, and sodium hydrogen phosphate (Na2HPO4), which serves as a weak base.
Sodium dihydrogen phosphate does not fully dissociate in neutral or acidic solutions. When a strong base, such as sodium hydroxide (NaOH), is introduced into the solution, sodium dihydrogen phosphate...
5.6K
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
769
Factors Affecting Solubility04:01

Factors Affecting Solubility

Compared with pure water, the solubility of an ionic compound is less in aqueous solutions containing a common ion (one also produced by dissolution of the ionic compound). This is an example of a phenomenon known as the common ion effect, which is a consequence of the law of mass action that may be explained using Le Chȃtelier’s principle. Consider the dissolution of silver iodide:
37.5K