在热应力下青路面的裂纹特性

If the temperature of an object is changed while it is prevented from expanding or contracting, the object is subjected to stress. The stress is compressive if the object expands in the absence of constraint and tensile if it contracts. This stress resulting from temperature change is known as thermal stress. It can be quite large and can cause damage. To avoid this stress, engineers may design components so they can expand and contract freely. For instance, on highways, gaps are deliberately...

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...

Concrete structures in cold climates, such as those along roadsides, can retain moisture. This moisture makes them susceptible to frost-related damage when temperatures fall below freezing. Adding moisture worsens the damage during temperature fluctuations, leading to repeated freezing and thawing. De-icing salts, spread over these structures to melt ice, add to the freeze-thaw cycle, and draw even more moisture into the concrete.
This freeze-thaw cycle primarily causes surface scaling, where...