Expanded and packed bed albumin adsorption on fluoride modified zirconia
A Mullick1, C M Griffith, M C Flickinger
1Biological Process Technology Institute, University of Minnesota, St. Paul, Minnesota, USA.
Abstract:
The expanded bed characteristics of 75-103microm fluoride-modified zirconia (FmZr) particles synthesized by a fed batch oil emulsion process were investigated. These particles are distinguished from commercially available expanded-bed adsorbents by virtue of their high density (2.8 g/cc) and the mixed mode protein retention mechanism which allows for the retention of both cationic and anionic proteins. The linear velocity versus bed porosity data agree with the Richardson-Zaki relationship with the terminal velocity in infinite medium of 2858.4 cm/h and a bed expansion index of 5.1. Residence time distribution (RTD) studies and bovine serum albumin (BSA) adsorption studies were performed as a function of the height of the settled bed to the column diameter (H:D) ratio and degree of bed expansion with superficial velocities of 440 to 870 cm/h. The settled bed, a 2x expanded bed, and a 3x expanded bed were studied for the H:D ratios of 1:1, 2:1, and 3:1. The dynamic binding capacity (DBC) at 5% breakthrough was low (2-8 mg BSA/mL settled bed) and was independent of the H:D ratio or the degree of bed expansion. The saturation DBC was 32.3 +/- 7.0 mg BSA/mL settled bed. The adsorption-desorption kinetics and intraparticle diffusion for protein adsorption on FmZr (38-75 micrometer) were investigated by studying the packed bed RTD and BSA adsorption as a function of temperature and flow rate. The data show that the adsorption-desorption kinetics along with intraparticle diffusion significantly influence protein adsorption on FmZr. Low residence times ( approximately 0.8 min) of BSA result in a DBC at 5% breakthrough which is 3.5-fold lower compared to that at 6-fold higher protein residence time. At low linear velocity (45 cm/h) the breakthrough curve is nearly symmetrical and becomes asymmetrical and more dispersed at higher linear velocity (270 cm/h) due to the influence of slow adsorption-desorption kinetics and intraparticle diffusion. Bioeng 60: 333-340, 1998.