Ultrasonic atomization for spray drying: a versatile technique for the preparation of protein loaded biodegradable...

Bovine serum albumin (BDA) loaded microspheres with a spherical shape and smooth surface structure were successfully prepared from poly(lactide-co-glycolide) using an ultrasonic nozzle installed in a Niro laboratory spray dryer. Process and formulation parameters were investigated with respect to their influence on microsphere characteristics, such as particle size, loading capacity, and release properties. Preparation of microspheres in yields of more than 50% was achieved using an ultrasonic atomizer connected to a stream of carrier air. Microsphere characteristics could be modified by changing several technological parameters. An increased polymer concentration of the feed generated larger particles with a significantly reduced initial release of the protein. Moreover, microspheres with a smooth surface structure were obtained from the organic polymer solution with the highest viscosity. Microparticles with a low BSA loading showed a large central cavity surrounded by a thin polymer layer in scanning electron microspheres. A high protein loading led to an enlargement of the shell layer, or even to dense particles without any cavities. A continuous in vitro release pattern of BSA was obtained from the particles with low protein loading. Glass transition temperatures (Tg) of the microspheres before and after lyophilization did not differ from those of the BSA loaded particles prepared by spray drying with a rotary atomizer. Analysis of the polymer by gel permeation chromatography indicated that ultrasonication had no effect on polymer molecular weight. Molecular weight and polydispersity of the pure polymer, placebo microspheres prepared by spray drying, and placebo microspheres prepared using the ultrasonic nozzle were in the same range. In conclusion, ultrasonic atomization represents a versatile and reliable technique for the production of protein loaded biodegradable microspheres without inducing a degradation of the polymer matrix. Particle characteristics can be modified by adjusting formulation parameters and atomization conditions in a simple manner.