Surfactant polymers designed to suppress bacterial (Staphylococcus epidermidis) adhesion on biomaterials

We describe a series of surfactant polymers designed as surface-modifying agents for the suppression of bacterial adhesion on biomaterials. The surfactant polymers consist of a poly(vinyl amine) backbone with hydrophilic poly(ethylene oxide) (PEO) and hydrophobic hexanal (Hex) side chains (PVAm/PEO:Hex). Surface modification is accomplished by simple dip coating from aqueous solution, from which surfactant polymers undergo spontaneous surface-induced assembly on hydrophobic biomaterials. The stability of PVAm/PEO:Hex on pyrolytic graphite (HOPG) and polyethylene (PE) was demonstrated by the absence of detectable desorption under flow conditions of pure water over a 24-h period. PEO surfactant polymers with four different PEO:Hex ratios (1:1.4, 1:2.5, 1:4.6, and 1:10.7) and a dextran surfactant polymer were compared with respect to S. epidermidis adhesion under dynamic flow conditions. Suppression of S. epidermidis adhesion was achieved for all modified surfaces over the shear range 0-15 dyn/cm(2). The effectiveness depended on the surfactant polymer composition such that S. epidermidis adhesion to modified surfaces decreased significantly with increasing PEO packing density. Modified HOPG was more effective in reducing bacterial adhesion compared with the corresponding modification on PE, which we attribute to the presence of defects in surfactant polymer assembly on PE. Our results are discussed from the perspective of critical factors, such as optimal PEO packing density and hydration thickness, that contribute to the effectiveness of surfactant polymers to shield a biomaterial from adhesive bacterial interactions.