In vitro study of the Nd:YAG laser effect on human dental enamel: optical and scanning electron microscope analysis
J E Pelino1, J B Mello, C P Eduardo
1Department of Restorative Dentistry, UNESP, São José dos Campos, Brazil. pelinoj@dentistry.ucsf.edu
Objective:
The Nd:YAG laser irradiation of dental enamel was evaluated in enamel demineralization experiments in a Streptococcus mutans culture media.
Summary Background Data:
Previous studies had shown that a continuous wave Nd:YAG laser at an energy of approximately 67 mJ may induce an increased acid resistance in human dental enamel when exposed to severe demineralization conditions.
Methods:
Enamel windows of 3 x 4 cm in the buccal surface were irradiated with a continuous wave Nd:YAG laser at a wavelength of 1,064 microns using energy densities of from 83.75 to 187.50 J/cm2. Enamel windows of 3 x 4 cm on the lingual surface served as control (without the laser irradiation). The enamel windows were then exposed to a Streptococcus mutans culture media at a temperature of 37 degrees C for 15 and 21 days. The laser effects and demineralization were examined both by optical microscopy and scanning electron microscopy (SEM).
Results:
A comparison between the lased and the unlased windows of enamel showed fusion and recrystalization of the enamel and increased acid-resistance in all groups irradiated with the Nd:YAG laser. On the other hand, the 3 x 4 delimited enamel surfaces from the control group (not irradiated with the Nd:YAG laser) showed 100% demineralization.
Conclusions:
These findings are consistent with the finding that laser irradiation of dental results in significant reduction of the effective solubility of enamel mineral.