Evaluation of systemic metal diffusion after spinal pedicular fixation with titanium alloy and stainless steel...

It is known that titanium alloys cause more extensive local metallosis due to fretting corrosion than stainless steel implants. The aim of the present study was to investigate possible systemic metal releases (Ti, Al, V, Cr, Ni) in sheep where L4-L5 were implanted with titanium alloy (Ti6Al4V, ASTM F 136) and stainless steel (AISI 316 L). 16 sheep were used: 8 were implanted with Ti6Al4V and 8 with stainless steel. At 6, 12, 24 and 36 months, the following examinations were performed: histology, atomic absorption spectrophotometry (AAS) and scanning electron microscopy (SEM), on liver, lung, kidney, brain, spleen and lumbo-aortic lymph nodes. Hair, urine and arteria blood samples were also analysed by AAS before implantation and at sacrifices. A histologic and ultrastructural study was performed on peri-implant tissues, too. Particular attention was paid to avoid contamination from dissection instruments or use of containers. In basal and in samples at 6 and 12 months, no metals were found in blood, urine, hair or other target tissues of the animals implanted with either Ti6Al4V or stainless steel. Regarding Al, V, Co and Ni, negative results in all tissues and body fluids were obtained also at 24 and 36 months. On the contrary, Ti traces were found in lumbo-aortic lymph nodes and lungs of one sheep only (10 and 30 ng/g, respectively) at 24 months. At 36 months, a systemic diffusion of Ti was observed in all tissues of both sheep instrumented with Ti6Al4V (2-16.5 ng/g), except for body fluids and hair. Metal research in target tissues by light and SEM micro-probe analysis provided negative results. Current data suggest that the amount of Ti found in organs after stable pedicular fixation is extremely low and not biologically available. This observation would lead us to exclude the hypothesis of any toxic reaction and such a release seems to be due to the passive diffusion through lymphatic fluids. Additional studies are needed to confirm if this long-term release of Ti particles might cause tissue damage.