Surface activity and film formation from the surface associated material of artificial surfactant preparations

Surfactant proteins B and C (SP-B and SP-C) are present in natural derived surfactant preparations used for treatment of respiratory distress syndrome. Herein the surface activity of an SP-C analogue (SP-C(LKS)), a hybrid peptide between SP-C and bacteriorhodopsin (SP-C/BR) and a model peptide (KL(4)) was studied with a captive bubble surfactometer (CBS). The peptides were mixed with either 1,2-dipalmitoyl-sn-glycero-3-phosphocholine (DPPC)/phosphatidylglycerol (PG) (7:3, by weight) or DPPC/PG/palmitic acid (68:22:9, by weight) at a concentration of 1 mg/ml in HEPES buffer, pH 6.9 and a polypeptide/lipid weight ratio of 0.02--0.03. In some lipid/peptide preparations also 2% of SP-B was included. Adsorption, monitored as surface tension vs. time for 10 min after bubble formation did not show discernible differences for the whole set of preparations. Equilibrium surface tensions of approximately 25 mN/m were reached after 5--10 min for all preparations, although those with SP-C/BR appeared not to reach end point of adsorption within 10 min. Area compression needed to reach minimum surface tension of 0.5--2.0 mN/m was least for the KL(4) preparation, about 13% in the first cycle. 3% SP-C(LKS) in DPPC:PG (7:3, by weight) reached minimum surface tension upon 27% compression in the first cycle. If DPPC:PG:PA (68:22:9, by weight) was used instead only 16% area compression was needed and 14% if also 2% SP-B was included. 3% SP-C(LKS) in DPPC:PG (7:3, by weight)+2% SP-B needed 34% compression to reach minimum surface tension. The replenishment of material from a surface associated surfactant reservoir was estimated with subphase depletion experiments. With the 2% KL(4) preparation incorporation of excess material took place at a surface tension of 25--35 mN/m during stepwise bubble expansion and excess material equivalent to 4.3 monolayers was found. When 2% SP-B was added to 3% SP-C(LKS) in DPPC:PG (7:3, by weight) the number of excess monolayers increased from 1.5 to 3.6 and the incorporation took place at 30--40 mN/m. When SP-B was added to 3% SP-C(LKS) in DPPC:PG:PA (68:22:9, by weight) the number of excess monolayers increased from 0.5 to 3.4 and incorporation took place at 40--50 mN/m. With 2% SP-C/BR incorporation took place at 40--45 mN/m, frequent instability clicks were observed and excess material of approximately 1.1 monolayer was estimated.