Gas chromatographic study of the volatile products from co-pyrolysis of coal and polyethylene wastes

The aim of this study was to determine the volatile products distribution of co-processing of coal with two plastic wastes, low-density polyethylene from agriculture greenhouses and high-density polyethylene from domestic uses, in order to explain the observed decrease in coal fluidity caused by polyethylene waste addition. Polymeric materials, although they are not volatile themselves, may be analysed by gas chromatography through the use of pyrolysis experiments. In this way, a series of pyrolysis tests were performed at 400 and 500 degrees C in a Gray-King oven with each of the two plastic wastes, one high-volatile bituminous coal and blends made up of coal and plastic waste (9:1, w/w, ratio). The pyrolysis temperatures, 400 and 500 degrees C, were selected on the basis of the beginning and the end of the coal plastic stage. The organic products evolved from the oven were collected, dissolved in pyridine and analysed by capillary gas chromatography using a flame ionization detector. The analysis of the primary tars indicated that the amount of n-alkanes is always higher than that of n-alkenes and the formation of the alkenes is favoured by increasing the pyrolysis temperature. However, this effect may be influenced by the size of the hydrocarbon. Thus, the fraction C17-C31 showed a higher increase of n-alkenes/n-alkanes ratio than other fractions. On the other hand, the difference between the experimental and estimated values from tars produced from single components was positive for n-alkanes and n-alkenes, indicating that co-pyrolysis of the two materials enhanced the chemical reactivity during pyrolysis and produced a higher conversion than that from individual components.