Phase, compositional, and morphological changes of human dentin after Nd:YAG laser treatment

Although techniques for repairing root fracture have been proposed, the prognosis is generally poor. If the fusion of a root fracture by laser is possible, it will offer an alternative to extraction. Our group has attempted to use lasers to fuse a low melting-point bioactive glass to fractured dentin. This report is focused on the phase, compositional, and morphological changes observed by means of X-ray diffractometer, Fourier transforming infrared spectroscopy, and scanning electron microscopy-energy dispersive X-ray spectroscopy in human dentin after exposure to Nd:YAG laser. The irradiation energies were from 150 mJ/ pulse-10 pps-4 s to 150 mJ/pulse-30 pps-4 s. After exposure to Nd:YAG laser, dentin showed four peaks on the X-ray diffractometer that corresponding to a-tricalcium phosphate (TCP) and beta-TCP at 20 = 30.78 degrees/34.21 degrees and 32.47 degrees/33.05 degrees, respectively. The peaks of a-TCP and beta-TCP gradually increased in intensity with the elevation of irradiation energy. In Fourier transforming infrared analysis, two absorption bands at 2200 cm(-1) and 2015 cm(-1) could be traced on dentin treated by Nd:YAG laser with the irradiation energies beyond 150 mJ/pulse-10 pps-4 s. The energy dispersive X-ray results showed that the calcium/phosphorus ratios of the irradiated area proportionally increased with the elevation of irradiation energy. The laser energies of 150 mJ/ pulse-30 pps-4 s and 150 mJ/pulse-20 pps-4 s could result in the a-TCP formation and collagen breakdown. However, the formation of glass-like melted substances without a-TCP at the irradiated site was induced by the energy output of 150 mJ/ pulse-10 pps-4 s. Scanning electron micrographs also revealed that the laser energy of 150 mJ/ pulse-10 pps-4 s was sufficient to prompt melting and recrystallization of dentin crystals without cracking. Therefore, we suggest that the irradiation energy of Nd:YAG laser used to fuse a low melting-point bioactive glass to dentin is 150 mJ/ pulse-10 pps-4 s.