Effects of demineralization depth on microtensile bond strength to human dentin
M F Nunes1, E J Swift, J Perdigão
1Department of Operative Dentistry, University of North Carolina at Chapel Hill, 27599-7450, USA.
Purpose:
To evaluate the effect of different phosphoric acid concentrations (10% and 37%) on the microtensile bond strengths (microTBS) of three dentin adhesive systems with different solvents (ethanol, acetone, or none).
Materials And Methods:
Eighteen third molars divided into six groups were ground flat to expose superficial dentin, which was polished to 600-grit. The bonding procedure was initiated using either of two phosphoric acid gels (10% and 37%). Three adhesive systems - Single Bond (SB), Prime & Bond NT (NT), and One Coat Bond (OC) - with different solvents (ethanol, acetone, or none, respectively) were used. After adhesive application, a cylinder of composite resin was built up. After 24 h water storage, each tooth was serially sectioned into thin rectangular sections (or "sticks") parallel to the long axis and with a mean cross-sectional area of 0.4 mm2. microTBS were determined using an Instron universal testing machine. Data were analyzed using two-way ANOVA and Duncan's test.
Results:
Mean bond strengths ranged from 66.1 MPa for 10%/ H3PO4 and SB to 43.8 MPa for 37% H3PO4 and OC. SB and OC tended to have slightly higher bond strengths when 10% H3PO4 was used. NT with 37% H3PO4 had a significantly higher microTBS (54.6 MPa) than NT with 10% H3PO4 (44.4 MPa).
Conclusion:
Etching dentin with 37% H3PO4 resulted in a significantly higher mean microTBS for the acetone-based adhesive NT. For both the ethanol- and water-based adhesive (SB) and the solvent-free adhesive (OC), acid concentration did not significantly affect bond strength.