Preparation, dosimetric characterisation and investigation of related TSL defect centres in Li3Po4:Mg,Cu phosphor

L3PO4:Mg,Cu, a low effective atomic number and high sensitivity TSL phosphor, has been prepared. Its TSL glow curve shows a major peak around 360 degrees C with minor peaks around 110 degrees C and 230 degrees C. The optimum concentrations of the dopants are found to be 200 ppm each. Its gamma sensitivity is 1.2 times as compared to CaSO4:Dy (0.1 mol%). The optimum preirradiation annealing treatment is found to be 650 degrees C, 15 min. Its PL emission shows a band at 370 nm with excitation band at 250 nm. Dose to TSL response shows that its response is linear up to the gamma dose of 100 Gy for irradiations carried out at RT. An irradiated sample shows a distinct new ESR signal, which is tentatively assigned to an electron/hole localised on one of the oxygen(s) of the phosphate group. Step annealing experiments show decay of the defect centre around 340 degrees C. This correlates well with the TSL peak around 360 degrees C.