Thermoluminescent response of ZrO2 + PTFE prepared in Mexico to 90Sr/90Y beta particles

Results of studying the thermoluminescent response of undoped ZrO2 + PTFE pellets irradiated with 90Sr/90Y beta particles are presented. Previously, TL characteristics of ZrO2 films doped with rare earths were studied. Phosphor powder was obtained by evaporating a solution of zirconium nitrate in ethanol. In order to stabilise the traps in ZrO2 this phosphor was submitted to different thermal treatments. Optimal thermal treatment consisted in heating at 1100 degrees C for 24 h. With this powder. pressing at room temperature a mixture (2:1) of ZrO2 and polytetrafluoroethylene (PTFE), pellets of 5 mm diameter and 0.8 mm thickness were made. The glow curve of ZrO2 + PTFE pellets exhibited two peaks at 200 and 250 degrees C: its TL response as a function of beta particles dose was linear in the range from 2 to 60 Gy. Repeatability over 10 cycles was 1.8%. Fading at room temperature was 3.8% per month.