Chick embryo anchored alkaline phosphatase and mineralization process in vitro

Bone alkaline phosphatase with glycolipid anchor (GPI-bALP) from chick embryo femurs in a medium without exogenous inorganic phosphate, but containing calcium and GPI-bALP substrates, served as in vitro model of mineral formation. The mineralization process was initiated by the formation of inorganic phosphate, arising from the hydrolysis of a substrate by GPI-bALP. Several mineralization media containing different substrates were analysed after an incubation time ranging from 1.5 h to 144 h. The measurements of Ca/Pi ratio and infrared spectra permitted us to follow the presence of amorphous and noncrystalline structures, while the analysis of X-ray diffraction data allowed us to obtain the stoichiometry of crystals. The hydrolysis of phosphocreatine, glucose 1-phosphate, glucose 6-phosphate, glucose 1,6-bisphosphate by GPI-bALP produced hydroxyapatite in a manner similar to that of beta-glycerophosphate. Several distinct steps in the mineral formation were observed. Amorphous calcium phosphate was present at the onset of the mineral formation, then poorly formed hydroxyapatite crystalline structures were observed, followed by the presence of hydroxyapatite crystals after 6-12 h incubation time. However, the hydrolysis of either ATP or ADP, catalysed by GPI-bALP in calcium-containing medium, did not lead to the formation of any hydroxyapatite crystals, even after 144 h incubation time, when hydrolysis of both nucleotides was completed. In contrast, the hydrolysis of AMP by GPI-bALP led to the appearance of hydroxyapatite crystals after 12 h incubation time. The hydroxyapatite formation depends not only on the ability of GPI-bALP to hydrolyze the organic phosphate but also on the nature of substrates affecting the nucleation process or producing inhibitors of the mineralization.