Precipitation hardening in a dental low-gold alloy

Age-hardening characteristics in a dental low-gold alloy composed of 40.0 wt% Au-35.0 wt% Ag-7.9 wt% Pd-7.0 wt% Cu-5.0 wt% In-3.5 wt% Zn-1.5 wt% Sn, were investigated by means of the hardness test, XRD study, SEM observations and EPMA. The following results were obtained. The age-hardening was characterized by a precipitation of Cu-rich alpha2 phase in the a phase. The softening that occurred following prolonged ageing was due to the heterogeneous formation of the fine nodular precipitates composed of the Ag-rich alpha1 phase and the Cu-rich alpha2 phase at the grain boundaries of the a phase.