In Vitro Evaluation of Speed Sintering and Glazing Effects on the Flexural Strength and Microstructure of Highly...

This study aimed to investigate the impact of speed sintering and glazing on the flexural strength and microstructure of multilayered 5 mol% yttria-stabilized (5Y-) zirconia, which remains unknown. Bar-shaped specimens (N = 600) were fabricated from 5Y-zirconia (FX; Ceramill Zolid FX ML, ST; Katana STML) by cutting, polishing, sintering (conventional and speed sintering), and then glazing. A flexural strength test (n = 30/group), field emission scanning electron microscopy (FE-SEM) observation (n = 2/group), and an X-ray diffraction (XRD) study with Rietveld refinement (n = 1/group) were performed. The flexural strength was analyzed using three-way ANOVA and a post hoc Scheffé test. The grain size was analyzed using the Kruskal-Wallis H test and Bonferroni-Dunn post hoc test. Flexural strength slightly decreased in the nonglazed FX after speed sintering (p < 0.05). Glazing with and without glazing paste did not affect flexural strength at both sintering speeds (p > 0.05). Speed sintering and glazing minimally changed the Weibull modulus and phase fraction, and did not affect grain size (p > 0.05). ST had a larger grain size and lower tetragonal phase content than FX and had a lower flexural strength than FX in most groups (p < 0.05). Overall, the multilayered 5Y-zirconia is considered suitable for dental application using speed sintering and glazing.