Rate and extent of aqueous perchlorate removal by iron surfaces

The rate and extent of perchlorate reduction on several types of iron metal was studied in batch and column reactors. Mass balances performed on the batch experiments indicate that perchlorate is initially sorbed to the iron surface, followed by a reduction to chloride. Perchlorate removal was proportional to the iron dosage in the batch reactors, with up to 66% removal in 336 h in the highest dosage system (1.25 g mL(-1)). Surface-normalized reaction rates among three commercial sources of iron filings were similar for acid-washed samples. The most significant perchlorate removal occurred in solutions with slightly acidic or near-neutral initial pH values. Surface mediation of the reaction is supported by the absence of reduction in batch experiments with soluble Fe2+ and also by the similarity in specific reaction rate constants (kSA) determined for three different iron types. Elevated soluble chloride concentrations significantly inhibited perchlorate reduction, and lower removal rates were observed for iron samples with higher amounts of background chloride contamination. Perchlorate reduction was not observed on electrolytic sources of iron or on a mixed-phase oxide (Fe3O4), suggesting that the reactive iron phase is neither pure zerovalent iron nor the mixed oxide alone. A mixed valence iron hydr(oxide) coating or a sorbed Fe2+ surface complex represent the most likely sites for the reaction. The observed reaction rates are too slow for immediate use in remediation system design, but the findings may provide a basis for future development of cost-effective abiotic perchlorate removal techniques.