Application of selective implantation in Al0.5Ga0.5As/In0.25Ga0.75As/GaAs pseudomorphic single quantum wire...

A pseudomorphic Al0.5Ga0.5As/In0.25Ga0.75As/GaAs asymmetric quantum wire (QWR) structure was grown on GaAs V-grooved substrate by low pressure metal organic vapor phase epitaxy. The formation of crescent shaped QWRs at the bottom of the V-grooves was confirmed by both transmission electron microscopy and photoluminescence (PL) spectra. The temperature dependence of PL spectra demonstrated a fast decrease of the sidewall quantum well PL intensity with increasing temperature, which originates from relaxation of carriers from well to wire region. The self-aligned dual implantation technique was successfully used to selectively disable the adjacent quantum structures. Decrease of the PL intensity of QWR at 8 K was observed after selective implantation, which resulted from a decreased number of carriers relaxed from adjacent quantum structures.