The effectiveness of cure of LED and halogen curing lights at varying cavity depths

This study compared the effectiveness of cure of two LED (light-emitting diodes) lights (Elipar FreeLight [FL], 3M-ESPE and GC e-Light [EL], GC) to conventional (Max [MX] (control), Dentsply-Caulk), high intensity (Elipar TriLight [TL], 3M-ESPE) and very high intensity (Astralis 10 [AS], Ivoclar Vivadent) halogen lights at varying cavity depths. Ten light curing regimens were investigated. They include: FL1-400 mW/cm2 [40 seconds], FL2-0-400 mW/cm2 [12 seconds] --> 400 mW/cm2 [28 seconds], EL1-750 mW/cm2 [10 pulses x 2 seconds], EL2-350 mW/cm2 [40 seconds], EL3-600 mW/cm2 [20 seconds], EL4-0-600 mW/cm2 [20 seconds] --> 600 mW/cm2 [20 seconds], TL1-800 mW/cm2 [40 seconds], TL2-100-800 mW/cm2 [15 seconds] --> 800 mW/cm2 [25 seconds], AS1-1200 mW/cm2 [10 seconds], MX-400 mW/cm2 [40 seconds]. The effectiveness of cure of the different modes was determined by measuring the top and bottom surface hardness (KHN) of 2-mm, 3-mm and 4-mm thick composite (Z100, [3M-ESPE]) specimens using a digital microhardness tester (n = 5, load = 500 g; dwell time = 15 seconds). Results were analyzed using ANOVA/Scheffe's post-hoc test and Independent Samples t-Test (p < 0.05). For all lights, effectiveness of cure was found to decrease with increased cavity depths. The mean hardness ratio for all curing lights at a depth of 2 mm was found to be greater than 0.80 (the accepted minimum standard). At 3 mm, all halogen lights produced a hardness ratio greater than 0.80 but some LED light regimens did not; and at a depth of 4 mm, the mean hardness ratio observed with all curing lights was less than 0.80. Significant differences in top and bottom KHN values were observed among different curing regimens for the same light and between LED and halogen lights. While curing with most modes of EL resulted in significantly lower top and bottom KHN values than the control (MX) at all depths, the standard mode of FL resulted in significantly higher top and bottom KHN at a depth of 3 mm and 4 mm. The depth of composite cure with LED LCUs was, therefore, product and mode dependent.