Electron holography of non-stained bacterial surface layer proteins

We report transmission electron microscopy (TEM) investigations on bacterial surface layers (S-layers) which belong to the simplest biomembranes existing in nature. S-layers are regular 2D protein crystals composed of single protein or glycoprotein species. In their native form, S-layers are weak phase objects giving only poor contrast in conventional TEM. Therefore, they are usually examined negatively stained. However, staining with heavy metal compounds may cause the formation of structural artefacts. In this work, electron microscopy studies of non-stained S-layers of Bacillus sphaericus NCTC 9602 were performed. Compared to other proteins, these S-layers are found relatively stable against radiation damage. Electron holography was applied where information about phase and amplitude of the diffracted electron wave is simultaneously obtained. In spite of small phase shifts observed, the phase image reconstructed from the hologram of the non-stained S-layer is found to be sensitive to rather slight structure and thickness variations. The lateral resolution, obtained so far, is less than that of conventional electron microscopy of negatively stained S-layers. It corresponds to the main lattice planes of 12.4 nm observed in the reconstructed electron phase image. In addition, as a unique feature of electron holography the phase image provides thickness information. Thus, the existence of double layers of the protein crystals could be easily visualized by the height profile of the specimen.