The hydrophilization of polystyrene substrates by 172-nm vacuum ultraviolet light

This paper describes the photochemical surface modification of polystyrene (PS) substrates using vacuum ultraviolet (VUV) light 172 nm in wavelength. We have particularly focused on the effects of atmospheric pressure during VUV irradiation on the obtained surface's wettability and the stability of the wettability, in addition to its chemical structure, morphology, and photooxidation rate. Samples were photoirradiated with VUV light under pressures of 10, 10(3), or 10(5) Pa. Although, in each case, the originally hydrophobic PS surface became highly hydrophilic, the final water-contact angle and photooxidation rate depended on the atmospheric pressure. The samples treated at 10 Pa were less wettable than those prepared at 10(3) and 10(5) Pa due to the shortage of oxygen molecules in the atmosphere. The minimum water-contact angles of the samples treated at 10, 10(3), and 10(5) Pa were about 8 degrees, 0 degrees, and 0 degrees, respectively. With the samples prepared at 10 and 10(3) Pa, photooxidation reactions proceeded in the topmost region closest to the surface, while at 10(5) Pa photooxidation was found to be greatly enhanced in the deeper regions, as evidenced by angle-resolved X-ray photoelectron spectroscopy. Photoetching rates were determined through atomic force microscope observation of microstructured PS samples prepared by a simple mesh-contact method. As estimated from AFM images of the latticed microstructures obtained, the rates of samples prepared at 10(3) and 10(5) Pa were about 1.5 and 1.3 nm/min, respectively. However, no photoetched features were observable on the sample surface prepared at 10 Pa. Hydrophilic stability also varied greatly depending on atmospheric pressure. The hydrophilicity of samples treated at 10 and 10(3) Pa gradually decreased as they were exposed to air. On the other hand, the sample surface prepared at 10(5) Pa showed excellent hydrophilicity even after being left in air for 30 days.