Microstructure and strength of extruded porous HA ceramics
M Rusnah1, M Andanastuti, B Idris
1Bahagian Teknologi Perubatan, Institut Penyelidikan Teknologi Nuklear Malaysia (MINT).
The Medical Journal of Malaysia
|October 8, 2004
Abstract:
The paper discusses the influence of sintering temperature on the microstructure and strength of hydroxyapatite ceramics prepared using the extrusion process. The average pore diameters observed were in the range of approximately 150mm to 300mm whereas the compaction strength was found to be around 120-160 MPa.
Related Concept Videos
01:18Porosity in Cement Paste
The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...
The balance of water to cement in the mix is critical—it...
01:29Strength and Heat of Hydration
The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...