Preparation of Pt-Re/Vulcan carbon nanocomposites using a single-source molecular precursor and relative performance
Angela D Anderson1, Gregg A Deluga, Joshua T Moore
1Department of Chemistry, Vanderbilt University, Nashville, Tennessee 37235, USA.
Abstract:
Pt-Re/Vulcan carbon powder nanocomposites have been prepared with total metal loadings of 18 wt.% and 40 wt.% using a new non-cluster (1:1)-PtRe bimetallic precursor as the source of metal. Pt-Re nanoparticles having an average diameter of ca. 6 nm and atomic stoichiometry near 1:1 are formed. TEM, on-particle HR-EDS, and powder XRD data are consistent with the formation of Pt-Re alloy nanoparticles having a hexagonal unit cell with cell constants of a = 2.77 A and c = 4.47 A. A nanocomposite prepared at higher total metal loading under more rigorous thermal treatment also contains Pt-Re alloy nanoparticles having a fcc unit cell structure (a = 3.95 A). The precise dependence of Pt-Re nanocrystal structure on the thermal history of the nanocomposite specimen has not been investigated in detail. While these Pt-Re/carbon nanocomposites are active as anode catalysts in operating direct methanol fuel cells, the measured performance is less than that of commercial Pt-Ru/carbon catalysts and has marginal practical importance.
More Related Videos
12:12On the Preparation and Testing of Fuel Cell Catalysts Using the Thin Film Rotating Disk Electrode Method
Published on: March 16, 2018
08:40Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production
Published on: December 6, 2021