On-chip free-flow magnetophoresis: continuous flow separation of magnetic particles and agglomerates

The separation of magnetic microparticles was achieved by on-chip free-flow magnetophoresis. In continuous flow, magnetic particles were deflected from the direction of laminar flow by a perpendicular magnetic field depending on their magnetic susceptibility and size and on the flow rate. Magnetic particles could thus be separated from each other and from nonmagnetic materials. Magnetic and nonmagnetic particles were introduced into a microfluidic separation chamber, and their deflection was studied under the microscope. The magnetic particles were 2.0 and 4.5 microm in diameter with magnetic susceptibilities of 1.12 x 10(-4) and 1.6 x 10(-4) m(3) kg(-1), respectively. The 4.5-microm particles with the larger susceptibility were deflected further from the direction of laminar flow than the 2.0-microm magnetic particles. Nonmagnetic 6-microm polystyrene beads, however, were not deflected at all. Furthermore, agglomerates of magnetic particles were found to be deflected to a larger extent than single magnetic particles. The applied flow rate and the strength and gradient of the applied magnetic field were the key parameters in controlling the deflection. This separation method has a wide applicability since magnetic particles are commonly used in bioanalysis as a solid support material for antigens, antibodies, DNA, and even cells. Free-flow magnetophoretic separations could be hyphenated with other microfluidic devices for reaction and analysis steps to form a micro total analysis system.