Related Experiment Video

Updated: Aug 18, 2026

Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives
08:40

Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives

Published on: May 17, 2020

Effect of fracture strength of primer-adhesive mixture on bonding effectiveness

Takatsumi Ikeda1, Jan De Munck, Kenichi Shirai

  • 1Leuven BIOMAT Research Cluster, Department of Conservative Dentistry, School of Dentistry, Oral Pathology and Maxillo-Facial Surgery, Catholic University of Leuven, Kapucijnenvoer 7, B-3000 Leuven, Belgium.

Dental Materials : Official Publication of the Academy of Dental Materials
|April 14, 2005
PubMed
Abstract

More Related Videos

Standardized Protocol to Evaluate the Effect of Surface Treatments, Luting Cements, and Thermocycling on PEEK–Composite Bond Strength04:23

Standardized Protocol to Evaluate the Effect of Surface Treatments, Luting Cements, and Thermocycling on PEEK–Composite Bond Strength

Published on: June 9, 2026

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
Tensile Strength Considerations of Concrete01:16

Tensile Strength Considerations of Concrete

Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
The dimensions and shape of a concrete specimen also...
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Impact Strength of Concrete01:21

Impact Strength of Concrete

Impact strength in concrete is a critical measure that reflects the material's capability to endure the forces applied during pile driving and when supporting machinery foundations that experience impulsive loads. It is also essential when handling precast concrete components to prevent accidental damage. The impact strength is assessed by observing the concrete's resistance to repeated impacts and energy absorption capacity. A key indicator of significant damage to concrete is when it does not...
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to the...