The shear bond strength between luting cements and zirconia ceramics after two pre-treatments

This study evaluated the shear-bond strength of 11 luting cements from different material classes to manufactured pre-treated zirconia ceramics (Lava: 97% ZrO2, stabilized with 3% Y2O3). In addition, the influence of the curing method on shear-bond strength was investigated. The cements examined were one zinc-phosphate cement (Fleck's zinc cement), two standard glass-ionomer cements (Fuji I, Ketac-Cem), three resin-modified glass-ionomer cements (Fuji Plus, Fuji Cem, RelyX Luting), four standard resin cements (RelyX ARC, Panavia F, Variolink II, Compolute) and one self-adhesive universal resin cement (RelyX Unicem). The ceramic surface was sand-blasted with 100-microm alumina or tribochemically coated with silica. After bonding procedure, one group was tested after 30 minutes (Time I), the other group was stored in distilled water at 37 degrees C for 14 days and subsequently thermocycled 1000 times (Time II). Statistical analysis was performed by multifactorial ANOVA models with interactions. For multiple pairwise comparisons, the Tukey method was used. After sandblasting, the highest shear-bond strength was obtained for the self-adhesive universal resin cement at 9.7 MPa (Time I) and 12.7 MPa (Time II), respectively. When using the Rocatec system, the highest values were found for one of the resin cements at 15.0 MPa (Time I) and for the self-adhesive universal resin cement at 19.9 MPa (Time II).