Adsorption of fluoride on zirconium(IV)-impregnated collagen fiber

A novel adsorbent, zirconium(IV)-impregnated collagen fiber, was prepared. Zr(IV) was uniformly dispersed in collagen fiber, mainly through chemical bonds, and was able to withstand the extraction of water. This adsorbent is effective for the removal of fluoride from aqueous solutions. The adsorption capacity was 2.29 mmol/g at pH = 5.5 when 5.00 mmol/L fluoride solution was adsorbed by use of 0.100 g of adsorbent, and the extent of removal was 97.4% when the adsorbent dose was 0.300 g. The adsorption isotherms were well fitted by the Langmuir equation, and the maximum adsorption capacities calculated by the Langmuir equation were close to those determined by experiment. The adsorption capacity increased with rising temperature. These facts imply that the mechanism of chemical adsorption might be involved in the adsorption process of fluoride on the absorbent and that fluorides are adsorbed in the form of monolayer coverage on the surface of the adsorbent. The adsorption kinetics of fluoride onto Zr(IV)-impregnated collagen fiber could be described by Lagergren's pseudo-first-order rate mode. The investigation on desorption indicated that this adsorbent is easily regenerated by use of dilute NaOH solution.