A temporary filling material may cause cusp deflection, infractions and fractures in endodontically treated teeth
M H Laustsen1, E C Munksgaard, C Reit
1Department of Cariology and Endodontics, School of Dentistry, Faculty of Health Sciences, University of Copenhagen, Copenhagen, Denmark. mhl@odont.ku.dk
Aim:
To test the hypothesis that Coltosol F might cause infractions and cusp fracture in root-filled teeth because of material expansion.
Methodology:
Thirty-two extracted human molar teeth were root filled and prepared with mesial-occlusal-distal (MOD) cavities with or without undercuts. The specimens were filled proximally with glass-ionomer cement and then occlusally with either Coltosol F or zinc oxide eugenol (ZOE). The tooth specimens were kept in water at 37 degrees C for a period of 20 days, and every second day the intercusp distance (ICD) of each specimen was measured in a travelling microscope, and the number of infraction lines as well as fractures were noted.
Results:
The number of infraction lines increased in teeth filled with Coltosol F. Between day 8 and 16, seven of 16 teeth filled with Coltosol F showed fracture and exhibited a mean increase in ICD of 316 +/- 156 microm. Teeth filled with ZOE did not show an increase in number of infraction lines or in ICD, and none showed fracture.
Conclusions:
The hygroscopic expansion of Coltosol F in a cavity may lead to cusp deflection, infraction development and fracture. Masticatory forces will in vivo aggravate this unfavourable condition. The material is not recommended for temporary filling in root-filled teeth except for a few days.