Effect of SiO2 coating layer morphology on TiH2 gas release characteristic

In this study, a uniform and compact SiO2 film-coating layer was prepared on the surface of TiH2 particles by sol-gel method using inexpensive raw materials. The preparation process of SiO2-coated TiH2 particles and the effect of the coating layer morphology on the gas release characteristic were investigated in detail. When the pH value of TiH2 suspending solution is about 4.0 and the concentration of silicic acid is more than 0.5 mol/L, the coating layer shows a SiO2 particle-coating morphology. While a homogeneous and dense film-coating layer can be obtained when the solution pH value and concentration of silicic acid are about 4.0 and 0.5 mol/L. The results of gas release at 700 degrees C show that TiH2 particles coated with silicon dioxide layers can efficiently delay the starting time of gas release of TiH2 powders to 60-100 s. Comparing the particle-coating layer, the SiO2 film-coating layer has a better delaying effect on gas release of TiH2 particles.