Microstructure and magnetic properties of Fe(x)Ni(1-x) alloy nanoplatelets

Plate-like nanoparticles (or nanoplatelets) of Fe(x)Ni(1-x) (x = 0.1, 0.2, 0.3, 0.4, 0.5, and 0.6) alloy were successfully synthesized through a simple sonochemical method. The shapes of the alloy nanoplatelets with different Fe atom contents are almost same. Their average diameters are about 50 nm, and their average thicknesses are several nanometers. The obtained Fe(x)Ni(1-x) alloy nanoplatelets are single-phased and have a face-centered cubic (FCC) crystal structure. The lattice constants of the alloy nanoplatelets are larger than the corresponding bulk value and increase with increasing Fe content. The surface oxidation of the alloy nanoplatelets leads to the lattice expansion. The alloy nanoplatelet powders are all ferromagnetic, and their saturation magnetizations are slightly lower than the corresponding bulk value. The saturation magnetic field and the coercivity increase with increasing Fe content. Magnetic hysteresis loops along the directions deviating different angles from the nanoplatelets plane are obviously different, indicating that the easy-axis is in the in-plane direction and the magnetization reversal is incoherent mode. The micromagnetic simulation results for the array composed of thirty-six Fe0.6Ni0.4 alloy nanoplatelets fit well with the measured data.