The effect of water absorption on acrylic surface properties
Hugh Devlin1, Prashant Kaushik
1Department of Restorative Dentistry, Temple University School of Dentistry, Philadelphia, USA. Hugh.Devlin@man.ac.uk
Purpose:
The aim of the present study was to determine whether an increased water content during thermal cycling of hot water-treated acrylic was associated with a reduction in surface hardness and an increased opacity or whitening of the surface.
Materials And Methods:
Ten acrylic samples were treated with 30 soak cycles (cycle duration, 24 hours), using warm water (40 degrees C) and an alkaline peroxide tablet (Efferdent control group); a further ten samples were treated with boiling water (100 degrees C) and one Efferdent tablet (experimental group). Indentation hardness of the acrylic specimens was measured prior to and immediately following the completion of the warm and hot water treatments, using an automated micro-indentation system. The hydrated acrylic specimens were then allowed to air dry at room temperature (20 degrees C) and were weighed weekly until they had obtained a constant dry weight. The loss in weight of the acrylic specimens represented the maximum water absorption.
Results:
The hot water-treated specimens were much whiter than the warm water-treated specimens. The mean reduction in hardness (H(IT)) of the acrylic specimens following the treatment with hot water and alkaline peroxide tablet was 12.9%. Treatment with warm water and alkaline peroxide resulted in a slight increase in mean hardness (2.63%). There was a significant correlation between the water content of the acrylic specimens after treatment and the percentage of change in indentation hardness (r= 0.495, p= 0.026).
Conclusions:
The hot water treatment of the acrylic was associated with a significant reduction in hardness. We attribute the whitening and reduction in the hardness of the hot water-treated specimens to absorption of water and a disruption of the acrylic surface structure.
Related Concept Videos
02:57Surface Tension, Capillary Action, and Viscosity
The various IMFs between identical molecules of a substance are examples of cohesive forces. The molecules within a liquid are surrounded by other molecules and are attracted equally in all directions by the cohesive forces within the liquid. However, the molecules on the surface of a liquid are attracted only by about one-half as many molecules. Because of the unbalanced molecular attractions on the surface molecules, liquids contract to form a shape that minimizes the number...
02:11Leveling Effect and Non-Aqueous Acid-Base Solutions
The Leveling Effect of a Solvent
A generic acid (HA) reacts with the generic base (B-) to yield the corresponding conjugate base (A-) and conjugate acid (HB):
02:45Acid-Catalyzed Hydration of Alkenes
01:20Porosity and Absorption of Aggregate
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the aggregate...
01:24Factors Affecting Workability
01:29Leveling Effect