Mechanical properties and bond strength of dual-cure resin composites to root canal dentin
Juthatip Aksornmuang1, Masatoshi Nakajima, Richard M Foxton
1Department of Prosthetic Dentistry, Faculty of Dentistry, Prince of Songkla University, Hat Yai, Songkhla 90112, Thailand. juthatip.a@psu.ac.th
Objectives:
To evaluate the regional mechanical properties of dual-cure resin composites and their regional bond strengths to root canal dentin.
Methods:
One of the following dual-cure resin composites was placed in artificial post spaces: Unifil Core (UC), Clearfil DC Core (DC), Build-It FR (BI), Clearfil DC Core-automix (DCA), and photo-cured for 60s. After 24h storage, each specimen was serially sliced to harvest eight hour-glass shaped specimens for measurement of regional ultimate tensile strength (UTS), and the remaining eight semi-circular slabs were polished for the measurement of Knoop Hardness Number (KHN). For the microtensile bond strength (muTBS) test, post cavities were prepared in human premolar roots, and the cavity surfaces treated with Clearfil SE Bond and photo-cured for 10s. The post spaces were then filled with one of the above resin composites and photo-cured for 60s. After 24h storage, each specimen was serially sliced into 8, 0.6x0.6 mm-thick beams for the muTBS test. The data were divided into coronal and apical regions and analyzed using ANOVA and post hoc test (alpha=0.05).
Results:
UTS and KHN were affected by the type of dual-cure resin composite and region (p<0.0001). There was no relationship between UTS and KHN for each material. The auto-mix type of resin composite possessed superior UTS to that of the hand-mix type. muTBS among the four composite materials were not significantly different at both apical and coronal regions (p>0.05). Regional differences in bond strengths were found for all materials (p<0.05).
Significance:
The UTS and KHN of the dual-cure resin composites varied among each material, however, differences in the mechanical properties of the resin core materials did not affect their adhesion to root canal dentin.
Related Concept Videos
01:17Mortar Properties
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
01:21Tooth Anatomy
The Crown, Neck, and Root
The visible part of the tooth is referred to as the crown. It's covered by enamel, the hardest substance in the human body. The crown is uniquely shaped for each type of tooth, allowing for different functions such as cutting, tearing, or grinding food.