Growth Kinetics of Thiobacillus thiooxidans on the Surface of Elemental Sulfur

The growth kinetics of Thiobacillus thiooxidans on elemental sulfur in batch cultures at 30(deg)C and pH 1.5 was studied by measuring the time courses of the concentration of adsorbed cells on sulfur, the concentration of free cells suspended in liquid medium, and the amount of sulfur oxidized. As the elemental sulfur was oxidized to sulfate ions, the surface concentration of adsorbed cells per unit mass of sulfur approached a maximum value (maximum adsorption capacity of sulfur particles) whereas the concentration of free cells continued to increase with time. There was a close relationship between the concentrations of free and adsorbed cells during the microbial sulfur oxidation, and the two cell concentrations were well correlated by the Langmuir isotherm with adsorption equilibrium constant K(infA) and maximum adsorption capacity X(infAm) of 2.10 x 10(sup-9) ml per cell and 4.57 x 10(sup10) cells per g, respectively. The total concentration of free and adsorbed cells increased in parallel with the amount of sulfate formed. The total growth on elemental sulfur gave a characteristic growth curve in which a linear-growth phase followed the period of an initial exponential phase. The batch rate data collected under a wide variety of inoculum levels (about 10(sup5) to 10(sup8) cells per ml) were consistent with a kinetic model assuming that the growth rate of adsorbed bacteria is proportional to the product of the concentration, X(infA), of adsorbed cells and the fraction, (theta)(infV), of adsorption sites unoccupied by cells. The kinetic and stoichiometric parameters appearing in the model were estimated from the experimental data, and the specific growth rate, (mu)(infA), and growth yield, Y(infA), were 2.58 day(sup-1) and 2.05 x 10(sup11) cells per g, respectively. The proposed model and the parameter values allowed us to predict quantitatively the surface attachment of T. thiooxidans cells on elemental sulfur and the bacterial growth in both initial exponential and subsequent linear phases. The transition from exponential to linear growth was a result of two competing factors: an increase in the adsorbed-cell concentration, X(infA), permitted a decrease in the unoccupied-site fraction, (theta)(infV).