Physiochemical properties of various polymer substrates and their effects on microchip electrophoresis performance

A suite of polymers were evaluated for their suitability as viable substrate materials for microchip electrophoresis applications, which were fabricated via replication technology. The relevant physiochemical properties investigated included the glass transition temperature (T(g)), UV-vis absorption properties, autofluorescence levels, electroosmotic flow (EOF) and hydrophobicity/hydrophilicity as determined by sessile water contact angle measurements. These physiochemical properties were used as a guide to select the proper substrate material for the intended microchip electrophoretic application. The T(g) of these polymers provided a guide for optimizing embossing parameters to minimize replication errors (REs), which were evaluated from surface profilometer traces. RE values ranged from 0.4 to 13.6% for the polymers polycarbonate (PC) and low-density polyethylene (LDPE), respectively. The absorption spectra and autofluorescence levels of the polymers were also measured at several different wavelengths. In terms of optical clarity (low absorption losses and small autofluorescence levels), poly(methyl methacrylate), PMMA (clear acrylic), provided ideal characteristics with autofluorescence levels comparable to glass at excitation wavelengths that ranged from 488-780 nm. Contact angle measurements showed a maximum (i.e., high degree of hydrophobicity) for polypropylene (PP), with an average contact angle of 104 degrees +/-3 degrees and a minimum exhibited by gray acrylic, G-PMMA, with an average contact angle of 27 degrees +/-2 degrees. The EOF was also measured for thermally assembled chips both before and after treatment with bovine serum albumin (BSA). The electrophoretic separation of a mixture of dye-labeled proteins including; carbonic anhydrase, phosphorylase B, beta-galactosidase, and myosin, was performed on four different polymer microchips using laser-induced fluorescence (LIF) excitation at 632.8 nm. A maximum average resolution of 5.04 for several peak pairs was found with an efficiency of 6.68 x 10(4) plates for myosin obtained using a BSA-treated PETG microchip.