Dendritic structures of poly(ethylene glycol) on silicon nitride and gold surfaces

A hydrophilic silicon nitride surface was grafted with poly(ethylene glycol) monomethyl ether (average formula weight of 5000 Da) in a one-step protocol. The domains of stable dendritic structures of self-assembled monolayer islands on a silicon nitride surface were observed with atomic force microscopy. The moduli of elasticity of these dendritic structures in air and in KCl aqueous solution were compared. The value of the Young's modulus of these structures is reduced by more than 3 orders of magnitude, from approximately 12 GPa measured in air to approximately 5 MPa in KCl solution. This dramatic reduction in elasticity was attributed to the swelling of the dendritic structures in aqueous solution, which was verified by the increased film thickness. These dendritic structures were not stable in the aqueous environment and could be removed by soaking in water for 22 h because of the hydrolysis of the silicate bonds. This fact was confirmed by the reduction of the C1s signal in the X-ray photoelectron spectroscopy experiments. These morphologies are not unique to silicon nitride substrate; similar features were also observed for thiolated poly(ethylene glycol) monomethyl ether molecules absorbed on a gold surface.